Ar400鋼の熱処理
AR400スチールプレート 組み合わせる carefully controlled chemical composition and precise heat treatment to deliver 高い耐摩耗性, 靭性, and industrial versatility.
理解する alloy composition and heat treatment process is essential for selecting the right steel plate for high-abrasion, heavy-duty applications.
- 説明
AR400 steel plate is a high-hardness, 広く使われている耐摩耗鋼 採掘, 工事, セメント, と重機 産業.
Its superior performance is achieved through careful alloy design and controlled heat treatment processes.
1. 化学組成
| 要素 | コンテンツ (%) | 関数 |
|---|---|---|
| 炭素 (C) | 0.20–0.25 | 硬度と耐摩耗性を提供します |
| マンガン (ん) | 1.2-1.5 | 靭性と焼入性の向上 |
| クロム (Cr) | 0.8-1.2 | Enhances wear resistance and corrosion protection |
| モリブデン (モー) | 0.2-0.3 | Improves toughness and high-temperature strength |
| ニッケル (で) | ~0.3 | Enhances impact toughness and ductility |
まとめ:
-
AR400 is a medium-carbon, low-alloy steel optimized for high hardness and impact resistance.
-
The chemical composition allows the plate to be 溶接された, カット, and fabricated 産業用途向け.
2. 機械的性質
| 財産 | Value |
|---|---|
| 硬度 (HB) | 400 ± 20 |
| 抗張力 (MPa) | 850–950 |
| 降伏強さ (MPa) | 550–700 |
| 衝撃靱性 (j) | 25–35 at room temperature |
Performance Highlights:
-
High abrasion resistance suitable for クラッシャーライナー, バケツ, ホッパー, そしてシュート
-
Good balance of 硬さと靱性 for high-impact environments
-
に適しています both industrial and heavy-duty applications
3. 熱処理工程
の AR400 plate achieves its performance through the following heat treatment steps:
-
焼入れ
-
The steel is heated to 900–950°C, then rapidly cooled in water or oil.
-
This produces a マルテンサイト構造, increasing hardness.
-
-
テンパリング
-
The quenched steel is reheated to 200–250°C and held to reduce brittleness.
-
Improves impact toughness while maintaining wear resistance.
-
-
表面処理
-
AR400 plates are often shot-blasted or ground to remove scale and prepare for welding or fabrication.
-
注意事項:
-
Proper heat treatment ensures consistent hardness across the plate.
-
厚さ, cooling rate, and alloy content influence the final hardness and toughness.
4. Fabrication and Applications
製作:
-
できる カット, 溶接された, and machined using standard industrial techniques.
-
Overlays and hardfacing can further enhance wear resistance.
アプリケーション:
-
鉱山機械: クラッシャーライナー, バケットライナー, ホッパー
-
工事: ミキサーブレード, コンベアライナー
-
Heavy machinery: ダンプトラックの車体, loader arms
-
Cement and metallurgy: フィードシュート, furnace liners