According to the welding characteristics of wear-resistant composite plates, the special flux-cored welding wire for wear-resistant composite plates developed by ourselves does not need to be cleaned after welding, the welding spatter is small, the plate surface is smooth and beautiful after welding, the welding efficiency is high, and the welding wire melting efficiency is more than 90%.
| 仕様 (mm) | HRC | Main Ingredients | Main uses and characteristics |
| 2.4、2.8、3.2 | 58-65 | C:3.0-5.0 Cr:16-21 | Used for single layer welding of wear-resistant plate, hardness of single layer after welding HRC58-63 |
| 2.4、2.8、3.2 | 57-63 | C:3.0-5.0 Cr:22-27 | Double-layer welding for wear-resistant plate surfacing. The hardness of double-layer welding is HRC58-63, which has good impact resistance and is not easy to fall off. |
| 2.4、2.8、3.2 | 57-63 | C:3.0-5.0 Cr:24-30 | 耐摩耗性プレートクラッドの多層溶接に使用されます。. 溶接の硬さ以上 3 層はHRC58-63です, 耐衝撃性に優れ、脱落しにくい. |
| 2.4、2.8、3.2 | 58-65 | C:3.0-5.0 Cr:16-21 | 極薄板の溶接に使用します。. 実際の溶接厚さが以下の場合 3 mm, 溶接後の硬度はHR58-63です。, 良好な耐摩耗性を確保する. |
| 2.4、2.8、3.2 | 58-65 | C:3.0-5.0 Cr:25-38 | 溶接後の溶着金属はクロム含有量が高く、耐摩耗性に優れています。 |