mn13(X120Mn12) Descripción general del acero con alto contenido de manganeso
Mn13 es un grado de acero chino, conocido por su excelente resistencia al impacto y la abrasión. Se utiliza comúnmente en industrias que requieren una alta resistencia al desgaste por impacto., como la minería, metalurgia, maquinaria vial, e ingenieria especial.
Key Specifications
- Calificación: mn13 (Porcelana), X120Mn12 (Europa), ASTM A128, 120mn12 (Alemania)
- Productos: Placas de acero con alto contenido de manganeso., round bars, flat bars, and wire.
- Available Stock Sizes:
- TISCO Plates: 2.0milímetros – 5.0MM GRISIÓN, 1000mm x 2000mm
- Baosteel Plates: 6.0milímetros – 20.0MM GRISIÓN, 2000mm x 6000mm
- Custom Orders: Plates with widths between 1500mm and 2440mm, lengths between 4000mm and 8000mm, can be made to order.
Composición química (%)
- Carbón (do): 1.00 – 1.30
- Silicio (Y): 0.25 – 0.50
- Manganeso (Minnesota): 11.00 – 14.00
- Azufre (S): ≤ 0.040
- Fósforo (PAG): ≤ 0.100
- Cromo (cr): 1.50
Propiedades mecánicas
- Resistencia a la tracción: 880 – 1130 MPa
- Fuerza de producción: ≥ 410 MPa
- Alargamiento: ≥ 40%
- Shock Absorption (Agua): 124 j (at room temperature)
- Dureza: ≤ 229 media pensión
Mn13 Characteristics
- Resistencia al impacto: Mn13 hardens upon impact, making it more resistant to wear over time.
- Resistencia a la abrasión: Ideal for industries that experience heavy wear and stress, such as shot blasting, minería, and road construction.
- Endurecimiento por trabajo: As the surface wears, a new hardening layer forms, ensuring continuous protection.
- Ease of Processing: It can be easily cut, soldado, doblado, y mecanizado, making it versatile for different applications.
Aplicaciones
Mn13 is widely used in machinery, equipo electrico, coal processing, and other high-wear industries. Its high impact resistance and excellent wear properties make it the best choice for reducing equipment maintenance costs and enhancing product competitiveness.
Tratamiento térmico
- Specification: Solid solution heat treatment ensures optimal mechanical properties.
|
do |
Y |
Minnesota |
PAG |
S |
cr |
|
1.0~1.3 |
0.3~0.5 |
11.0~14.0 |
≤0.100 |
≤0.040 |
(≤1,50) |
METRO
|
tensile strength Rm(Mqa) |
yield strength Re(MPa) |
reduction of area A(%) |
ballistic work Akv(j) |
|
880~1130 |
≥410 |
≥40 |
124(normal temperature) |
Teda Ganghua Metal -18 años
Proporcionar productos profesionales resistentes al desgaste.
Proveedor resistente al desgaste
Traiga especificaciones detalladas a contactame si lo necesitas
Tenemos alta calidad y precios razonables.