中国の耐摩耗鋼板を理解する

耐摩耗性の鋼板を理解する

Wear-resistant steel plates are specialized products designed for use in high-wear environments. 硬い層を厚く塗布することで作られています。, 通常の低炭素鋼または低合金鋼の表面に耐摩耗性材料を塗布. この組み合わせにより、耐久性に必要な靭性と可塑性が得られます。.

What is the Material of Wear-Resistant Steel Plates?

The primary material is steel, consisting of a low-carbon base plate and an alloy wear-resistant layer. This wear-resistant layer typically makes up about 1/2 に 1/3 of the plate’s thickness and is rich in chromium. The chromium content can reach 20% に 30%, resulting in a high surface hardness and excellent wear resistance, extending the product’s service life.

主な特徴

耐衝撃性: Wear-resistant plates have strong impact resistance. They can endure significant drops during material transport without sustaining serious damage.
耐熱性: These plates can typically be used at temperatures below 600 degrees Celsius. If vanadium and platinum are added during manufacturing, they can withstand high temperatures up to 800 degrees without issues.
耐食性: The high chromium content also gives wear plates excellent corrosion resistance, minimizing worries about degradation.
費用対効果: Although wear-resistant plates are 1 に 2 times more expensive than standard steel plates, they last over 10 倍以上長い. This longevity makes them a cost-effective choice.
Easy Processing: Wear-resistant plates are highly weldable and can be bent into various shapes, making them convenient to work with.

Standards and Manufacturers

Wear-resistant steel plates conform to the GB/T24186-2009 standard. Notable manufacturers include Wuhan Iron and Steel, 宝鋼, Nangang, Xinsteel, and Laigang.

学年	厚さ	幅	長さ
NM360	8	2200	8000
NM360	10	2200	8000
NM360	15	2200	8000
NM400	12	2200	8000
NM500	16	2200	8000
NM360	20	2200	10300
NM450	25	2200	12050
NM400	30	2200	8000
NM360	35	2090	10160
NM400	40	2200	8000
NM400	45	2200	8000
NM400	50	2200	8000
NM360	60	2200	7000
NM360	135	0635	2645
NM400	70	2200	9500
NM400	80	2200	8000

Main Grades and Thicknesses

Common grades include NM360, NM400, NM450, そして NM500, 厚さの範囲は次のとおりです 6 mm to 40 mm.

機械的性質

NM360: 硬度 330-390 HBW, yield strength ≥900 MPa, tensile strength ≥1100 MPa.
NM400: 硬度 370-430 HBW, yield strength ≥1000 MPa, tensile strength ≥1200 MPa.
NM450: 硬度 420-480 HBW, yield strength ≥1100 MPa, tensile strength ≥1250 MPa.
NM500: Hardness ≥470 HBW, yield strength ≥1200 MPa, tensile strength ≥1500 MPa.

結論

Wear-resistant steel plates offer numerous advantages for various applications. Their durability, 耐熱性, and corrosion protection make them ideal for challenging conditions. By choosing wear-resistant plates, users can enhance their operations and ensure long-lasting performance.