X120MN12 내 입력 강판

개요:

X120Mn12 (Mn13) 고 충격적이고 스트레스가 많은 마모 애플리케이션에 이상적인 자료입니다.. 이 강철에는 두 가지 주요 특성이 있습니다: 외부 충격이 증가하면 내마모성이 더욱 높아집니다., 그리고 표면이 마모되면서, 새로운, 더 조밀한 적층층이 연속적으로 형성됨, 내구성 강화. The steel offers excellent resistance to both high-impact and heavy-stress abrasion, without risk of breaking during use. It is also easy to cut, 용접하다, 그리고 구부려라, offering superior mechanical processing properties. Unlike high-chrome forgings, which only resist wear from moving abrasion, X120Mn12 provides broader resistance in various applications.

응용:

This steel is commonly used in wear-prone parts of machinery, helping to reduce equipment maintenance costs and increasing competitiveness by enhancing performance.

주요 기능:

11-14% 망간 함량.
Excellent work-hardening properties.
Ideal for high-impact and gouging abrasion environments.
Available in full plates or cut pieces.
Non-magnetic and abrasion-resistant.

형성:

X120Mn12 steel is ductile in its supplied form, making it easy to shape. To avoid cracking, edges that have been work-hardened by shearing should be chamfered 2-3mm before forming. For best results, forming should be done in a single operation to prevent additional work hardening.

교련:

Drilling X120Mn12 is challenging due to its 11-14% 망간 함량, which causes rapid work hardening. Heavy-duty, rigid machinery is required. Use armor-piercing drills made from 8% cobalt high-speed steel, or drills with replaceable carbide inserts. Avoid center-punching or letting the drill rub against the surface without engagement, as this will further harden the material and complicate drilling.

용접:

Welding should be performed with E308Mo-type austenitic stainless steel consumables. Due to the high manganese content, this steel has a high thermal expansion coefficient and low thermal conductivity. Welding should be done at low heat to prevent embrittlement caused by carbide precipitation, which can occur if the material is exposed to temperatures between 300°C and 800°C for prolonged periods.