1.3401 Placa de aço material
1.3401 material é um aço austenítico com alto teor de manganês with excellent wear resistance and toughness, suitable for high-impact and abrasive applications. It belongs to a broader family of manganese steels including X120Mn12, MN13, and Hadfield steel, all of which share the key feature of surface work-hardening combined with a tough, núcleo dúctil.
- Descrição
1.3401 is a high manganese austenitic steel widely used for wear-resistant and impact-resistant applications. Its high manganese content stabilizes the austenitic structure, giving it exceptional toughness, forte capacidade de endurecimento, and excellent abrasion resistance.
It is commonly used in heavy-duty environments such as mining, cimento, revestimentos do britador, e máquinas de terraplenagem.
Chemical Composition of 1.3401
The chemical composition of 1.3401 is carefully balanced to ensure both resistência ao desgaste e tenacidade:
| Elemento | Faixa Típica (% em peso) | Função |
|---|---|---|
| Carbono (C) | 1.10 – 1.40 | Aumenta a dureza e o endurecimento da superfície |
| Manganês (Mn) | 11.0 – 14.0 | Estabilização de Austenita, resistência, resistência ao desgaste |
| Silício (E) | ≤ 1.0 | Desoxidação, melhora a força |
| Fósforo (P) | ≤ 0.07 | Impureza controlada |
| Enxofre (S) | ≤ 0.03 | Impureza controlada |
| Cromo (Cr) | ≤ 2.0 | Melhora a dureza e a resistência à corrosão |
| Níquel (Em) | ≤ 1.0 | Melhora a resistência |
| Ferro (Fé) | Equilíbrio | Metal básico |
Mechanical Properties and Wear Resistance
| Propriedade | Valor típico |
|---|---|
| Força de rendimento | 350 – 450 MPa |
| Resistência à tracção | 750 – 1100 MPa |
| Alongamento | ≥ 35% |
| Dureza (solução tratada) | 180 – 220 HB |
| Dureza (trabalho endurecido) | Até 500 HB |
Wear-Resistant Features:
-
Work-hardens under repeated impact
-
Não magnético em condição tratada com solução
-
Resistência e ductilidade de alto impacto
-
Excellent abrasion resistance after surface hardening
Other Common Manganese Steel Grades
-
X120Mn12 / DE 1.3401 – European standard high manganese steel for heavy wear and impact applications.
-
MN13 – Chinese GB standard, similar to X120Mn12, widely used in mining and crushers.
-
Hadfield Aço – Classic manganese steel with 12–14% Mn and 1.0–1.4% C, known for extreme work-hardening.
-
X100Mn12 / Mn12 – Slightly lower carbon content, endurecimento moderado, suitable for chutes and conveyors.
-
X120Mn13 – High manganese steel with enhanced toughness and wear resistance, often used in heavy-duty liners.
Tabela Resumo: Comparison of Manganese Steel Grades
| Nota | Mn Content (% em peso) | C Content (% em peso) | Dureza (HB) | Recurso principal | Aplicações |
|---|---|---|---|---|---|
| 1.3401 / X120Mn12 | 11–14 | 1.10–1.40 | 180–220 (solução tratada) | Endurecimento do trabalho, alta resistência ao desgaste | Revestimentos do britador, forros de caçamba |
| MN13 | 11–13 | 1.05–1.30 | 170–210 | Similar to X120Mn12 | Equipamento de mineração, placas de impacto |
| Hadfield Aço | 12–14 | 1.0–1.4 | 180–220 | Classic manganese steel | Placas de mandíbula, moinhos |
| X100Mn12 | 11–12 | 0.9–1,2 | 160–200 | Dureza moderada | Cataratas, transportadores |
| X120Mn13 | 11–14 | 1.2–1.4 | 180–220 | Enhanced toughness | Forros para serviços pesados, tremonhas |