Wear Plate AR400 AR450 AR500 NM360 NM400 NM500 Wear

NM450 NM400 NM500 Abrasion Resistant Steel Plate

NM400 NM500 Mn13 40Cr abrasion resistant steel plate

Thickness 5mm to 120mm Abrasion Resistant Steel Plates

Wear Plate AR400 AR450 AR500 NM360 NM400 NM500 Wear Resistant Steel Sheet Plate Price

Abrasion-resistant steel grade with greater surface hardness than AR400, while retaining good ductility and formability.

Surface Hardness: 410-490 BHN
Applications: Suitable for moderate to heavy wear environments, including bucket components, dump truck bodies, and construction equipment.
Alternate Name: Also known as AR450F (formable).
Manufacturing Note: Composition and hardening processes vary by mill; mill test reports are provided with each order.

Category: wear resistant plates

Description

Wear resistant steel are produced from processes of hot rolling, cutting into length and heat treating. The products are characterized with small thickness, good flatness, outstanding wear resistance, excellent toughness, good weldability, good machinablility, consistent property and quality.
Wear resistant steels are developed for applications where high wear resistant performance is required, such as dumper, garbage vehicle, concrete mixer truck, industrial air fan, hopper, crusher, machinery for coal, grain, cement, grab bucket, etc.

Industrial AR (NM) Steel Plate

Abrasion-resistant steel plate is widely used across industries such as energy, industrial manufacturing, and infrastructure. Key applications include:

Mining
Construction
Material Handling

With its versatility in wear-resistant applications—from shooting targets to dump buckets—Teda maintains an extensive inventory of AR steel plates at its distribution centers to meet diverse industry needs.

NM400 Wear-Resistant Steel Sheet is a wear resistant steel with good comprehensive properties like high strength, high hardness, good wear resistance and weld ability etc .
NM400 Wear-Resistant Steel Plate & Sheets are demanded widely by many commercial industries as they offer great wear resistance, high strength and thus significantly improving wear resistance of heavy mechanical parts.

Chemical Composition,/%
Grade	C	Si	Mn	P	S	Cr	Ni	Mo	Ti	B	AlS
Grade	≤									Range	≥
NM360	0.25	0.70	1.60	0.025	0.015	0.80	0.50	0.50	0.05	0.0005-0.006	0.01
NM400	0.30	0.70	1.60	0.025	0.010	1.00	0.70	0.50	0.05	0.0005-0.006	0.01
NM450	0.35	0.70	1.70	0.025	0.010	1.10	0.80	0.55	0.05	0.0005-0.006	0.01
NM500	0.38	0.70	1.70	0.02	0.010	1.20	1.00	0.65	0.05	0.0005-0.006	0.01

Mechanical Properties
Grade	Thickness/mm	Rm/Mpa	A50/%	-20℃KV2/Jitudinal)	HBW
NM360	≤80	≥1100	≥12	≥24	330-390
NM400	≤80	≥1200	≥10	≥24	370-430
NM450	≤80	≥1250	≥7	≥24	420-480
NM500	≤70	≥1300	≥7	≥24	480-520