Chromium Carbide Wear Plates
Chromium Carbide Wear Plates
Common chromium carbide wear plates are produced by flux cored arc welding. These plates are ideal for applications involving high abrasion and low to medium impact.
|
Chemicals |
Hardness |
Sheet Size |
Base Metal |
|
C – Cr – Fe |
HRC 58-63 |
1400*3400 |
Q235/Q345. etc |
| Chemical Composition(%) |
C |
Cr |
Mn |
Si |
Fe |
Other |
|
3.0-5.0 |
15.0-35.0 |
1.0-3.0 |
1.0-3.0 |
Bal. |
– |
|
| Hardness |
HRC 58-65 |
|||||
| Standard Thickness(mm) |
3+3; 4+4; 5+5; 6+4; 6+6; 8+4; 8+6; 8+8; 10+10; 12+12; etc (overlay thickness up to 50mm) |
|||||
| Standard Sheet Size(mm) |
1400*3400; 1500*3000; 2000*3000; (Customized size available) |
|||||
| ASTM G65 Procedure A |
0.12 – 0.18g |
|||||
| Operating Temperature |
<400 ℃ |
|||||
| Base Metal Material |
Q235B, Q345B; A36; S235JR and structural steels |
|||||
| Main Industry |
Mining, glass industry, cement plant, steel mill, power plant, etc |
|||||
| Fabrication |
Plasma cutting, Gouging, Countersunk, stud bolt, Bending |
|||||
Customization
The plates can be customized in various sizes and thicknesses based on customer drawings. Additionally, the wear plates can be cut, bent, and welded into specific shapes and parts.
Characteristics
- Chromium carbide overlay wear-resistant plate
- Chemical Composition: C: 3.0-5.0%, Cr: 18-30%
- Chromium carbide Cr7C3 volume fraction: Approximately 40%
- Wear-resistant layer thickness: Up to 50 mm
- Heat resistance: Up to 600°C
- Standard wear-resistant area sizes: 14003400 mm, 15003000 mm, 2000*3000 mm
- Flatness: Better flatness with a smooth surface
- Hardness: HRC58-65
These characteristics ensure durability and reliability in demanding environments.
Teda Ganghua Metal -17 years
Steel Sheets/Plates Supplier
Bring detailed specifications to contact me if you need
We have high quality and reasonable prices
📧 [email protected]
Whatsapp: +86 15822676888
Welcome to our website! https://www.tedametal.com/ & https://www.teda-metal.com/ & https://www.teda-aluminum.com/